RESUMO
Background: Soft denture lining materials act as a cushion between the denture base and tissues. Alongside having many advantages, its main problem is candida growth due to its rubbery and porous texture. Many interventions have been performed to halt the growth of candida within soft lining materials such as the use of antifungal therapy and strict oral and denture hygiene but there are consequences such as recurrence, drug resistance, and toxicity related to these interventions. Since natural agents such as aloe vera and chitosan have been proven to have antibacterial and antifungal properties with minimum adverse effects, this study aimed to study the effectiveness of chitosan and aloe vera powders incorporated within denture soft lining materials against candida adherence. Methodology. A total of 60 soft-lining material samples were prepared that were equally divided into three groups, viz., group 1 (chitosan incorporation), group 2 (aloe vera incorporation), and group 3 (control). Candida was obtained from the microbiology lab to form a candidal suspension, diluted in 0.9% NaCl to match the McFarland standard bacteriologic solution. Samples were incubated at 37°C for 24 hours in test tubes containing 100 mL of the candidal suspension and 9.9 mL of the previously prepared Sabouraud dextrose agar. Crystal violet stain was used to stain the adhering cells by fixing them with methanol 80%. For each sample, the adhering candida cells were counted on three standard fields by using an inverted light microscope, and the mean of those fields was recorded. Results: The mean value for samples containing aloe vera was 41.15, while the mean values for samples containing chitosan and the control group were 16.05 and 79.1, respectively. Of all the three groups, aloe vera powder had a significant efficacy against candida growth as compared to the chitosan and control groups (P value = 0.001). Conclusion: Both herbal agents were effective against candida growth. In comparison, aloe vera was more effective against candida growth compared to chitosan.
RESUMO
Aim: In recent years, great advances have been made in the use of CAD/CAM to prepare fixed restorations. The marginal and internal fit of these restorations is a principal determinant for their clinical success. In addition, the nature of the oral environment affects the mechanical properties of these restorations. Therefore, this study aimed to investigate the effect of aging process under conditions that simulate the oral environment on the marginal adaptation, and, fracture resistance of crowns fabricated from polyether ether ketone (PEEK) using CAD/CAM methods. Methods: Twenty identical crown restorations were fabricated by using CAD/CAM methods to mill polyether ether ketone (PEEK) material. These crowns were produced by using a software design of an epoxy resin replica of the prepared maxillary first premolar tooth. All PEEK crowns were cemented and randomly divided into two equal groups (A, B). Each group was divided into subgroups (A1, A2 and B1, B2). Group A1 and A2 were used to measure marginal adaptation and fracture resistance, respectively, before aging, while group (B1 and B2) were measured after aging. The cemented crowns were mounted in resin molds to facilitate the sectioning process. The measurements of the marginal gap were performed after sectioning at four points using a stereomicroscope. The fracture resistance of the crowns was investigated using a universal testing machine. A statistical analysis was performed using the GraphPad Prism® software version and unpaired Student's t-test. Results: The results revealed that aging affected the marginal gap, and the fracture resistance of the PEEK crowns. While aging, negatively affected the conditions under investigation, however the least significant difference of marginal gap was found in the margin region. Conclusions: PEEK-CAD/CAM is considered as a good alternative prosthodontic material for fixed prostheses. The CAD/CAM technique used to make PEEK crown restorations in our study offers the advantages of high marginal accuracy and fracture resistance for long-term performance in the oral environment
